305 stainless steel pipe has good corrosion resistance and can stay stable in various corrosive media. The oxide film formed on its surface can effectively prevent the contact between the corrosive medium and the material, thereby extending the service life of the material. 305 stainless steel is also known for its good heat resistance as it shows stable performance at high temperatures. High amount of nickel element adds to the heat resistance of the material, making it less prone to deformation, oxidization under high temperatures. In addition, it can withstand greater pressure and impact due to the high strength and hardness, making it less likely to deform or break when under pressure. 305 stainless steel pipe is often used in the chemical industry, food processing, construction, aerospace, marine engineering, and other fields.
Product Parameters
| Product Name | 305 Stainless Steel Pipe | |
| Type | Steel Pipe | |
| Outer diameter | Round Tube | 4mm-200mm |
| Square Tube | 10*10mm-100*100mm | |
| Rectangular Tube | 10*20mm-50*100mm | |
| Wall Thickness | 0.6mm-6.0mm | |
| Length | 1-6 meters, Length can be customized | |
| Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
| Surface | Black, Bright Polished, Rough Turning, Matt Surface Treatment, No. 4. BA, etc. | |
| Scope of Application | Common applications for stainless steel pipes include food processing, Textile operations, Breweries, Water treatment plants, Oil and gas processing, Fertilizers and pesticides, Chemical applications, Construction, Pharmaceuticals, Auto parts, etc. | |
| Certificate | ISO, SGS, BV, etc. | |
| Production Technology | Hot Rolling, Cold Rolling | |
| Edge Processing | Edging, Trimming | |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P |
| ≤ 0.04 | ≤ 0.75 | ≤ 2.0 | 17.0～19.0 | 10.5～13.0 | ≤ 0.03 | ≤ 0.045 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥515 | ≥205 | ≥35 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
| 7.99 | 193 | 17.3 | 16.2 | 72 |