316 stainless steel pipe is recognized in the stainless industry for a number of key reasons. Grade 316 is the standard molybdenum-bearing austenitic grade, which is strongly invulnerable to pitting and crevice corrosion in chloride environments. So 316 stainless steel is commonly adopted in situations where higher corrosion resistance is required. For example, 316 stainless steel is often used to manufacture ship parts, subsea pipelines, offshore platforms and other facilities. In the chemical industry, it is also commonly used to produce equipment such as storage tanks, reactors and pipelines. In addition, 316 stainless steel is also widely used to manufacture medical devices and implants due to its excellent biocompatibility and corrosion resistance.
Product Parameters
| Product Name | 316 Stainless Steel Pipe | |
| Type | Steel Pipe | |
| Outer diameter | Round Tube | 4mm-200mm |
| Square Tube | 10*10mm-100*100mm | |
| Rectangular Tube | 10*20mm-50*100mm | |
| Wall Thickness | 0.6mm-6.0mm | |
| Length | 1-6 meters, Length can be customized | |
| Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
| Surface | Black, Bright Polished, Rough Turning, Matt Surface Treatment, No. 4. BA, etc. | |
| Scope of Application | Common applications for stainless steel pipes include food processing, Textile operations, Breweries, Water treatment plants, Oil and gas processing, Fertilizers and pesticides, Chemical applications, Construction, Pharmaceuticals, Auto parts, etc. | |
| Certificate | ISO, SGS, BV, etc. | |
| Production Technology | Hot Rolling, Cold Rolling | |
| Edge Processing | Edging, Trimming | |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P | Mo |
| ≤ 0.03 | ≤ 0.75 | ≤ 2.0 | 16.0～18.0 | 10.0～14.0 | ≤ 0.03 | ≤ 0.045 | 2.0～3.0 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥480 | ≥177 | ≥ 40 | ≤ 187HB;≤ 90HRB;≤ 200HV |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
| 7.99 | 193 | 16.0 | 16.2 | 74 |