310S stainless steel pipe has good oxidation resistance, corrosion resistance, acid and alkali resistance given its high content of nickel (Ni) and chromium (Cr). The strength is improved due to its solid solution strengthening effect after adding the content of carbon in austenitic stainless steel,. The chemical composition characteristics of austenitic stainless steel are based on chromium and nickel to add molybdenum, tungsten, niobium and titanium, and because of its face-centered cubic structure, it has high strength and creep strength at high temperatures. 310S stainless steel is often used in the manufacture of boiler, steam turbine, industrial furnace and aviation, petrochemical.
Product Parameters
| Product Name | 310S Stainless Steel Pipe | |
| Type | Steel Pipe | |
| Outer diameter | Round Tube | 4mm-200mm |
| Square Tube | 10*10mm-100*100mm | |
| Rectangular Tube | 10*20mm-50*100mm | |
| Wall Thickness | 0.6mm-6.0mm | |
| Length | 1-6 meters, Length can be customized | |
| Standard | ASTM, AISI, JIS, GB, DIN, EN, etc. | |
| Surface | Black, Bright Polished, Rough Turning, Matt Surface Treatment, No. 4. BA, etc. | |
| Scope of Application | Common applications for stainless steel pipes include food processing, Textile operations, Breweries, Water treatment plants, Oil and gas processing, Fertilizers and pesticides, Chemical applications, Construction, Pharmaceuticals, Auto parts, etc. | |
| Certificate | ISO, SGS, BV, etc. | |
| Production Technology | Hot Rolling, Cold Rolling | |
| Edge Processing | Edging, Trimming | |
Chemical Composition
| C | Si | Mn | Cr | Ni | S | P |
| ≤ 0.08 | ≤1.0 | ≤ 2.0 | 24.0～26.0 | 19.0～22.0 | ≤ 0.03 | ≤ 0.045 |
Mechanical Properties
| Tensile Strength Kb (MPa) | Yield Strength σ0.2 (MPa) | Elongation D5 (%) | Hardness |
| ≥520 | ≥205 | ≥40 | ≤ 217HB;≤ 95HRB |
Physical Performance
| Density(g/cm³) | Modulus of Elasticity(Gpa) | Coefficient of Thermal Expansion(10-6/°C) | Coefficient of Thermal Conductivity(W/m*K) | Resistivity(ΜΩ. cm) |
| 9.01 | 200 | 14.4 | 13.8 | 94 |